• Has good hot melt property and impact strength
• Has a certain degree of flexibility, so it can directly use 3D printing to manufacture equipment parts
• Highest heat, toughness and chemical resistance
• Excellent abrasion resistance, biocompatibility, chemical stability
• With high strength, good flexibility and high temperature resistance, the products printed with it have good surface quality, good dimensional stability, and are not easy to shrink
• Excellent polypropylene-like properties for printing moving parts,Snap engaging parts and small boxes and containers
| ACMEMFG Engineering Model |
WL55 |
| color |
White |
| Density (g/cm3 @ 25 ℃) |
1.13 |
| Curing depth (mm) |
0.13 |
| Critical exposure (mJ/cm2) |
11 |
| Construction layer thickness (mm) |
0.1 |
| Hardness (D) |
80 |
| Flexural modulus (MPa) |
2300-2800 |
| Bending strength (MPa) |
80-100 |
| Tensile modulus (MPa) |
|
| Tensile strength (MPa) |
52-58 |
| Elongation at break |
10-15 |
| Notched impact strength (J/m) |
20-30 |
| Heat distortion temperature (℃) |
50-55 |
| Glass transition temperature (℃) |
65 |